6013 T4 T6 Aluminum Sheet
The strength is higher than ordinary 6 series aluminum alloys and it maintains excellent corrosion resistance. Therefore, this alloy has a wide range of uses in aviation, ships, and transportation fields.
Some parts that are difficult to form, such as engine covers, are usually made of 2024. Switching to 6013 aluminum alloy can greatly reduce heat treatment costs.
6013 T4 T6 aluminum sheet dimensions and stock list
| Thickness/in | Metric Thickness/mm | Width*Length/mm |
|---|---|---|
| 0.032 | 0.813 | 609.6 x 1219.2 |
| 0.04 | 1.016 | 1219.2 x 1219.2 |
| 0.04 | 1.016 | 1219.2 x3657.6 |
| 0.05 | 1.27 | 1219.2 x 1219.2 |
| 0.063 | 1.60 | 1219.2 x 3657.6 |
| 0.071 | 1.803 | 609.6 x 1219.2 |
| 0. 10 | 1.20 | 1219.2 x 3657.6 |
| 0. 125 | 3.175 | 1219.2 x 1219.2 |
6013 T4 T6 aluminum sheet mechanical property
| Temper | T6 | T4 |
|---|---|---|
| Tensile strength | 470 MPa | 380 MPa |
| Yield strength | 390 MPa | 325 MPa |
| Elongation | 7% | 10% |
| Hardness (HB) | 130 | 100 |
| Bending strength | 600 MPa | 450 MPa |
| Fatigue strength | 150 MPa | 125 MPa |
6013 aluminum sheet chemical composition
| Element | Composition % |
|---|---|
| Si | 0,6-1,0 |
| Fe | 0,5 |
| Cu | 0,6-1,1 |
| Mn | 0,2-0,8 |
| Mg | 0,8-1,2 |
| Cr | 0,10 |
| Zn | 0,25 |
| Ti | 0,10 |
| Other each | 0,05 |
| Other total | 0,15 |
| Al | Rest |
6013 T4 T6 aluminum sheet thermal properties
| Melting point | Thermal Conductivity | Specific heat capacity |
|---|---|---|
| 580°C(1050°F) | 150 W/(m·K) | 900 J/kg-K |
Application Of 6013 T4 T6 aluminum sheet
3c electronic products field
6013 aluminum alloy is often used to manufacture electronic equipment housings and radiators. Due to its good conductivity and heat dissipation properties, it can ensure the normal operation and long-term stable performance of electronic equipment. At the same time, the lightweight properties of al6013 also help reduce the size and weight of electronic devices.
6013 aluminum alloy thin sheets are mainly used in shell parts and key components of 3C products. The forming methods are mostly rolling and extrusion.
Aerospace field
Such as manufacturing fuselage skins, webs, rear pressure cabin skins, and a variety of complex-shaped vertical tails and trailing edge fins.
Automobile manufacturing field
In automobile manufacturing, materials are required to be both lightweight and have sufficient strength and rigidity. Al6013 aluminum alloy exactly meets this requirement. It mainly used in structural parts that require welding, such as automobile bodies and frames and engine parts, it is favored for its good welding performance.